Pertumbuhan, Kekuatan Tarik Dan Mulur Serat Rami (Boehmeria Nivea (L.) Gaudich) Dengan Pemberian Asam Giberelat (Ga3) Dan Variasi Ketersediaan Air

Oleh :
Shafi Fauzi Rahman - M0405057 - Fak. MIPA

PERTUMBUHAN, KEKUATAN TARIK DAN MULUR SERAT RAMI (Boehmeria nivea (L.) Gaudich) DENGAN PEMBERIAN ASAM GIBERELAT (GA3) DAN VARIASI KETERSEDIAAN AIR ABSTRAK Tanaman rami (Boehmeria nivea) merupakan tanaman tahunan yang mudah tumbuh dan berkembang baik di daerah tropis. Serat rami mempunyai kekuatan yang lebih tinggi dibanding dengan serat kapas, sehingga tidak mudah putus, serat rami ini lebih sedikit mengalami penyusutan dibanding dengan serat-serat yang lain, kelembaban serat rami dapat mencapai 12%, serat rami bersifat halus, tahan lama dan kilatannya seperti sutera. Penelitian ini menggunakan rancangan acak lengkap (RAL) dengan dua faktor yaitu GA3 dengan 3 variasi konsentrasi (G) yaitu: 0 ppm, 175 ppm, 200 ppm, dan ketersediaan air dengan 3 variasi ketersediaan air (A) yaitu: 50%, 75%, 100%. Perlakuan diberikan pada rhizoma sebelum ditanam dan perlakuan ketersediaan air diberikan waktu tunas telah terbentuk. Parameter yang diukur adalah parameter pertumbuhan dan kualitas serat. Kesimpulan penelitian ini adalah perlakuan GA3 berpengaruh terhadap peningkatan panjang tunas, berat kering, berat basah, uji tarik serat (kekuatan serat), tetapi tidak berpengaruh terhadap jumlah tunas, jumlah daun dan mulur serat. Perlakuan ketersediaan air tidak berpengaruh terhadap semua parameter. Interaksi antara GA3 dan ketersediaan air berpengaruh terhadap mulur serat rami (B. nivea). Pemberian GA3 pada konsentrasi 200 ppm menunjukkan pengaruh terbaik pada semua parameter pertumbuhan dan kualitas serat yang diamati kecuali pada berat basah dan berat kering. Perlakuan ketersediaan air pada KL 100% menunjukkan pengaruh yang baik pada berat basah dan berat kering, pada KL 75% menunjukkan pengaruh yang baik pada kemampuan mulur serat. Kata Kunci: Asam giberelat (GA3), ketersediaan air, Boehmeria nivea, pertumbuhan, uji tarik dan mulur. THE GROWTH, PULLING AND ELASTICITY STRENGTH OF HEMP FIBER Boehmeria nivea (L.) Gaudich WITH APPLICATION OF GIBERELIC ACID GA3 AND WATER AVAILABILITY ABSTRACT Hemp plant Boehmeria nivea is an annual plant which is easy to grow and to reproduce in a tropical region. Hemp fiber has a higher strength than cotton fiber, so that it is not easily broken off. It provides less reduction than another fibers, the humidity of hemp fiber can achieve 12%, and hemp fiber has smooth characteristic, long lasting, and its glint is similar with the silk. This research used complete random design CRD using two factors that were GA3 with 3 concentration variations G, such as 0 ppm, 175 ppm, 200 ppm, and 3 water availability variations A), such as 50%, 75%, 100%. The treatment was given to the rhizome before it was planted and the water availability was given when the shoot was started to form. The measured parameters were parameter of growth and fiber quality. The conclusion of this research is that GA3 treatment has an influence toward the increase of shoot stem height, dry weight, wet weight, fiber pulling test fiber’s strength, but it has no influence in the change of shoot number, leaf number, and elasticity of the fiber. The water availability treatment has no influence toward the entire parameter. The interaction between GA3 and water availability has influence toward hemp B. nivea fiber elasticity. The giving of GA3 in the concentration of 200 ppm shows the best influence toward the entire parameter of growth and fiber quality observed except in wet weight and dry weight. Water availability treatment in SQ 100% shows good influence toward wet weight and dry weight, in SQ 75% it shows a good influence toward the elasticity of the fiber. Key words: Giberelat Acid GA3, water availability, Boehmeria nivea, growth, pulling and elasticity test.