Abstrak


Karakterisasi dan penentuan bobot tuang mg/al hydrotalcite dari brine water tiruan


Oleh :
Muhammad Yanwar P - M. 0307056 - Fak. MIPA

Telah dilakukan penelitian tentang sintesis, karakterisasi kimia dan fisika Mg/Al hydrotalcite yang disintesis dari brine water tiruan sebagai sediaan farmasi. Penelitian ini bertujuan untuk mengetahui apakah Mg/Al hydrotalcite dapat disintesis dari brine water tiruan dan mengetahui bagaimana karakterisasi kimia dan fisika Mg/Al hydrotalcite dari brine water tiruan dibandingkan dengan Mg/Al hydrotalcite murni sebagai bahan untuk sediaan farmasi. Mg/Al hydrotalcite disintesis dengan metode pengendapan, perbandingan rasio mol Mg/Al adalah 2:1. Brine water tiruan yang telah dihilangkan Ca2+ direfluks selama 1 jam pada suhu ±700C dengan pH 10. Karakterisasi dari Mg/Al hydrotalcite menggunakan X-Ray Diffraction (XRD) dan Fourier Transform Infra Red (FTIR). Karakterisasi kimia dan fisika yang dilakukan meliputi berat jenis nyata, berat jenis benar, berat jenis mampat, pH, kelarutan, faktor hausner, porositas, kompresibilitas, dan kandungan lembab. Variasi pH yang digunakan pada uji kelarutan adalah 1, 2, 3, dan 4. Hasil penelitian menunjukan bahwa untuk Mg/Al hydrotalcite hasil sintesis memiliki berat jenis nyata sebesar 0,649 g/mL, berat jenis mampat sebesar 0,758 g/mL, berat jenis benar sebesar 1,618 g/mL memiliki pH 8,92, kelarutan berturut-turut dari variasi pH 1 sampai 4 yaitu 92,00%, 29,00%, 8,40%, 3,00%, factor hausner 1,168, porositas 59,89%, kompresibilitas 14,38%, dan kandungan lembab 11,86%. Untuk Mg/Al hydrotalcite murni memiliki berat jenis nyata sebesar 0,538 g/mL, berat jenis mampat sebesar 0,687 g/mL, berat jenis benar sebesar 1,641 g/mL memiliki pH 8,91, kelarutan berturut-turut dari variasi pH 1 sampai 4 yaitu 94,40%, 25,60%, 8,80%, 0,86%, faktor hausner 1,277, porositas 67,22%, kompresibilitas 21,69% dan kandungan lembab 10,62%. A research has been conducted on the synthesis, chemical and physical characterization of Mg/Al hydrotalcite synthesized from counterfeit brine water as a pharmaceutical preparation. This research aims to find out whether or not Mg/Al hydrotalcite can be synthesized from the counterfeit brine water and to find out how the chemical and physical characterization of Mg/Al hydrotalcite from counterfeit brine water is compared with the pure Mg/Al hydrotalcite as pharmaceutical preparation. Mg/Al hydrotalcite was synthesized using precipitation method, with mol ratio of Mg/Al of 2:1. Counterfeit brine water, the Ca2+ of which had been removed, was refluxed for 1 hour at ±70oC at pH 10. The characterization of Mg/Al hydrotalcite was done using X-Ray Diffraction (XRD) and Fourier Transform Infra Red (FTIR). The chemical and physical characterizations were done encompassing the real density, true density, compressed density, pH, solubility, hausner factor, porosity, compressibility, and moisture content. The variations of pH used in solubility test were 1, 2, 3, and 4. The result shows that Mg/Al hydrotalcite as the result of synthesis had the real density of 0.649 g/mL, compressed density of 0.758 g/mL, true density of 1.618 g/mL, pH of 8.92; the solubility for each variation of pH from 1 to 4 was 92,00%, 29,00%, 8.40%, 3,00%, respectively; hausner factor of 1.168, porosity of 59.89%, compressibility of 14.38%, and moisture content of 11.86%. Meanwhile, pure Mg/Al hydrotalcite had the real density of 0.538 g/mL, compressed density of 0.687 g/mL, true density of 1.641 g/mL, pH of 8.91; the solubility for each variation of pH from 1 to 4 was 94.40%, 25.60%, 8.80%, 0.86%, respectively; hausner factor of 1.277, porosity of 67.22%, compressibility of 21.69%, and moisture content of 10.62%.