Pengaruh Fraksi Volume dan Ukuran Butir terhadap Kekuatan Bending dan Ketangguhan Impak Komposit Ripoxy R-802 – Serbuk Genteng Sokka


Oleh :
Muhadzib Mashur - I0407050 - Fak. Teknik

ABSTRAK
Tujuan dari penelitian ini adalah untuk mengetahui pengaruh kandungan
dan ukuran partikel serbuk genteng Sokka terhadap kekuatan bending dan
ketangguhan impak komposit Ripoxy R-802 – serbuk genteng Sokka.
Serbuk genteng Sokka (SGS) terbuat dari reject genteng Sokka yang hancur
menjadi serbuk kemudian serbuk itu diayak untuk menghasilkan empat variasi
variasi ukuran, lolos mesh 80 tertahan pada mesh 120 (180-125 µm), lolos mesh
120 tertahan pada mesh 150 (125-104 µm), lolos mesh 150 tertahan pada mesh
200 (104-74 µm), dan lolos mesh 200 (≤75 µm). SGS dipanaskan dalam oven
selama 45 menit pada suhu 105 °C. Lalu, serbuk dicampur dengan Ripoxy R-
802 dengan metode cetak tekan. Variasi dari fraksi volume SGS 10%, 20%,
30%, dan 40%. Pengujian kekuatan bending dan ketangguhan impak komposit
ini didasarkan atas standar ASTM D-6272 dan ASTM D-5941.
Hasil dari penelitian ini adalah sebagai berikut: (1) Penambahan serbuk
genteng Sokka sampai 20% pada komposit Ripoxy R-802 – SGS dapat
meningkatkan nilai kekuatan bending, modulus bending, ketangguhan impak,
dan energi serap (2) Pengaruh ukuran partikel SGS menunjukkan bahwa ukuran
partikel SGS yang semakin kecil akan menyebabkan peningkatan nilai
ketangguhan impak dan bending.
Kata kunci: Serbuk genteng Sokka (SGS), Ripoxy R-802, impak izod,
ketangguhan impak, kekuatan bending
ABSTRACT
The objective of this research is to investigate the effect of the content and
particle size on the bending strength and impact toughness of Ripoxy R-802 –
Sokka roof tile powder composites.
The Sokka tile powder (STP) was made from rejected Sokka roof tile which
was crushed into powder. The powder was sieved to result in four size
variances, which were mesh 80 retained in mesh 120 (180-125 µm), mesh 120
retained in mesh 150 (125-104 µm), mesh 150 retained in mesh 200 (104-74
µm), and breaking away from mesh 200 (≤74 µm). STP was heated in an oven
for 45 minutes in the temperature 105 °C. Afterwards, the powder was mixed
with Ripoxy R-802 at 50 rpm by 2-5 minutes. The variables in this research
were particle size (-80/+120, -120/+150, -150/+200, -200) and particle content
(0%, 10%, 20%, 30%, 40% in volume). The bending strength and impact
toughness testing on the composite was conducted on the basis of standard of
ASTM D-6272 and ASTM D-5941.
The results of this research are as follows: (1) Composites Ripoxy R-802
with 20% of STP content has the strongest values of bending strength and
impact toughness. The addition of STP content is able to increase the value of
impact toughness and bending strength to 20% (v/v) (2) The small size of the
particle of STP can increase the bending strength and value toughness Ripoxy
R-802 – STP composites.
Keywords: Sokka tile powder (STP), Ripoxy R-802, impact izod, impact
toughness, four point bending