Uji kualitas fisik dan uji kinetika reaksi briket kayu kalimantan merbau dengan penambahan jerami padi

Penulis Utama : Nuzul Wahyudi
NIM / NIP : I0405007
× Abstrak Penelitian ini dilakukan untuk mengetahui pengaruh penambahan jerami padi pada sifat fisik briket kayu Kalimantan merbau. Briket campuran kayu kalimantan merbau dan jerami padi dibuat dengan dua variasi komposisi (persentase berat), yaitu 80% kayu Kalimantan merbau ditambah 20% jerami padi dan 60% kayu kalimantan merbau ditambah 40% jerami padi. Proses pembriketan dilakukan dengan 4 variasi tekanan pembriketan, yaitu 400 kg/cm2, 600 kg/cm2, 800 kg/cm2, dan 1000 kg/cm2. Sifat fisik yang diuji dari masing-masing komposisi briket adalah densitas awal dan densitas relaksasi, relaksasi, ketahanan, kuat tekan aksial, serta ketahanan terhadap air. Hasil pengujian sifat fisik menunjukkan bahwa penambahan jerami padi mampu meningkatkan nilai kuat tekan aksial briket kayu kalimantan merbau. Hasil pengujian sifat-sifat fisik digunakan untuk menentukan tekanan pembriketan yang menghasilkan briket optimum untuk masing-masing komposisi. Hasil penelitian menunjukkan bahwa briket optimum diperoleh pada tekanan pembriketan 800 kg/cm2 untuk masing-masing komposisi. Uji kinetika reaksi dilakukan terhadap briket-briket optimum dengan 2 variasi kecepatan udara memasuki reaktor yaitu 0,05 m/s dan 2 m/s, pada temperatur reaktor 400oC. Profil pembakaran dari masing-masing komposisi briket telah diperoleh melalui pengujian kinetika reaksi. Dari uji tersebut, diperoleh pula nilai energi aktivasi dan faktor pre-eksponensial briket campuran. Nilai energi aktivasi untuk briket 80% kayu Kalimantan merbau yang ditambah 20% jerami padi adalah 11,93 kJ/mol untuk variasi kecepatan udara 2 m/s dan 15,29 kJ/mol untuk kecepatan udara 0,05 m/s. Sedangkan untuk briket 60% kayu Kalimantan merbau yang ditambah 40% jerami padi adalah 10,00 kJ/mol dan 13,96 kJ/mol. Kata kunci: briket, kayu Kalimantan merbau, jerami padi, densitas, energi aktivasi. Abstract This research was conducted to investigate the effect of rice straw addition on the physical properties of Borneo-merbau wood briquette. The briquettes which made from Borneo-merbau wood and rice straw were mixed with two variations of composition (weight percentage), i.e. 80% of Kalimantan-merbau wood added with 20% of rice straw and 60% of Kalimantan-merbau wood added with 40% of rice straw. Briquetting process was done by four briquetting pressure, that were 400 kg/cm2, 600 kg/cm2, 800 kg/cm2, and 1000 kg/cm2. Physical properties investigated from each composition of the briquettes were initial density, relaxation density, relaxation, durability, axial compressive strength, and water resistance. The experimental result showed that the addition of rice straw could increase the axial compressive strength of Borneo-Merbau wood briquettes. The results in physical properties were used to determine the briquetting pressure that could produce optimum briquette for each composition. From the result showed that optimum briquettes were obtained on briquetting pressure of 800 kg/cm2 for each composition. The reaction kinetics testing was done on the optimum briquettes with two-different air velocities which entering the reactor, that were 0.05 m/s and 2 m/s and at reactor temperature of 4000C. Combustion profile of each briquettes composition was obtained from reaction kinetic testing. Activation energy and pre-exponential factor of the briquettes could also be obtained from the testing Activation energy values of 80% Borneo-Merbau wood with 20% rice straw briquette were 11.93 kJ/mol and 15.29 kJ/mol, for 2 m/s and 0.05 m/s air velocity, respectively. Activation energy of 60% Borneo-Merbau wood with 40% rice straw briquette was 10.00 kJ/mol and 13.96 kJ/mol. Keywords: briquette, Borneo-Merbau wood, rice straw, density, activation energy
×
Penulis Utama : Nuzul Wahyudi
Penulis Tambahan : -
NIM / NIP : I0405007
Tahun : 2010
Judul : Uji kualitas fisik dan uji kinetika reaksi briket kayu kalimantan merbau dengan penambahan jerami padi
Edisi :
Imprint : Surakarta - F. Teknik - 2010
Program Studi : S-1 Teknik Mesin
Kolasi :
Sumber : UNS-F. Teknik Jur. Teknik Mesin-I.0405007-2010
Kata Kunci :
Jenis Dokumen : Skripsi
ISSN :
ISBN :
Link DOI / Jurnal : -
Status : Public
Pembimbing : 1. Suyitno, S.T., M.T., Dr.Tech.
2. Tri Istanto, S.T., M.T.
Penguji :
Catatan Umum : 14/2010
Fakultas : Fak. Teknik
×
File : Harus menjadi member dan login terlebih dahulu untuk bisa download.