Kajian pengaruh waktu adsorpsi gliserol pada alumina berdasarkan konsentrasi adsorbat

Penulis Utama : Wahyu Purnomo
NIM / NIP : M0305064
× ABSTRAK Telah dilakukan penelitian adsorpsi gliserol dengan mengunakan γ-Alumina sebagai adsorben, yang dilakukan berdasarkan pengamatan tegangan permukaan serta variasi konsentrasi dan variasi waktu adsorpsi. Penelitian ini bertujuan untuk mengetahui pengaruh tegangan permukaan terhadap adsorpsi, serta untuk mengatahui waktu optimum adsorpsi yang terjadi berdasarkan konsentrasi optimum gliserol. Pengamatan tegangan permukaan dilakukan pada variasi konsentrasi gliserol pada perbandingan gliserol:akuades 1:2, 1:3, 1:4 dan 1:5. Proses adsorpsi dilakukan dengan variasi konsentrasi gliserol perbandingan gliserol:akuades 1:2, 1:3, 1:4 dan 1:5, variasi waktu adsorpsi pada 2 jam, 4 jam, 6 jam, 8 jam dan 10 jam. Penentuan tegangan permukaan dilakukan dengan metode pipa kapiler. Interaksi antara gliserol dalam larutan dengan γ-Alumina dilakukan dengan metode batch. Aktivasi γ-Alumina dilakukan secara fisika dengan pemanasan pada suhu 400 oC selama 1 jam. Karakterisasi γ-Alumina dilakukan dengan menggunakan XRD, uji kemampuan adsorpsi dilakukan dengan uji keasaman dengan menggunakan NH3 sebagai adsorbat. Penentuan jumlah gliserol teradsorp dilakukan dengan menggunakan Kromatografi Gas (GC). Hasil penelitian menunjukkan bahwa tegangan permukaan semakin turun dengan meningkatnya konsentrasi gliserol dalam larutan. Kondisi optimum dari proses adsorpsi diperoleh pada konsentrasi gliserol tertinggi, serta pada proses adsorpsi gliserol 6 jam. Kapasitas adsorpsi maksimum pada variasi konsentrasi 1:2. Kapasitas adsorpsi maksimum pada variasi waktu adsorpsi 6 jam adalah 6,253 g/g. Kata kunci: adsorpsi, gliserol, γ-Alumina. v ABSTRACT Research of glycerol adsorption which used γ-Alumina as adsorbent was carried out, this experiment was done based on monitoring of surface tension and variation of concentration and also variation of adsorption time. This experiment was done to knew the influence of surface tension in adsorpstion and also to get optimal time of adsorption based on optimal concentration of glycerol. The monitoring of surface tension was performed in concentration variation of glycerol in comparison of glycerol:aquadest at 1:2, 1:3, 1:4 and 1:5. Adsorption process was done in concentration variation of glycerol in comparison of glycerol:aquadest at 1:2, 1:3, 1:4 and 1:5 and also in time variation of glycerol adsorption at 2, 4, 6, 8 and 10 hours. The monitoring of surface tension used capillary pipe methode. The interactions between glycerol and γ-Alumina were conducted in batch methode. Activation of γ-Alumina was done by physical methode by heats until 400 0C in 1 hours. Characteristic of γ-Alumina was analyzed by XRD, test of adsorption ability was analyzed used acidity test which used NH3 as adsorbate. Determination of glycerol amount was permeated in γ-Alumina used Gas Chromatography (GC). The result showed that surface tension was increased when glycerol concentration in solution was decreased. The optimal conditon of adsorption was performed in highest concentration of glycerol and also in time variation at 6 hours. The optimal of adsorption capacity in concentration variation at 1:2. The optimal of adsorption capacity in time variation at 6 hours was 6.253 g/g. Key words: adsorption, glycerol, γ-Alumina. vi
×
Penulis Utama : Wahyu Purnomo
Penulis Tambahan : -
NIM / NIP : M0305064
Tahun : 2010
Judul : Kajian pengaruh waktu adsorpsi gliserol pada alumina berdasarkan konsentrasi adsorbat
Edisi :
Imprint : Surakarta - FMIPA - 2010
Program Studi : S-1 Kimia
Kolasi :
Sumber : UNS-FMIPAJur. Sains Kimia-M.0305064-2010
Kata Kunci :
Jenis Dokumen : Skripsi
ISSN :
ISBN :
Link DOI / Jurnal : -
Status : Public
Pembimbing : 1. Yuniawan Hidayat, M.Si.
2. Dr. rer. nat. Atmanto Heru W., M.Si.
Penguji :
Catatan Umum : 3893/2010
Fakultas : Fak. MIPA
×
File : Harus menjadi member dan login terlebih dahulu untuk bisa download.