Pengaruh Media Pendingin Dan Temperatur Pemanasan Terhadap Nilai Kekerasan Grinding Ball Hasil Pengecoran

Saputro, Danang

× Danang Saputro. PENGARUH MEDIA PENDIGIN TEMPERATUR PEMANASAN TERHADAP NILAI KEKERASAN GRINDING BALL HASIL PENGECORAN Tujuan penelitian ini adalah untuk mengetahui: (1) Ada tidaknya perbedaan pengaruh media pendingin / quenching terhadap nilai kekerasan grinding ball hasil pengecoran. (2) Ada tidaknya perbedaan pengaruh temperatur pemanasan terhadap nilai kekerasan grinding ball hasi pengecoran. (3) Ada tidaknya perbedaan pengaruh interaksi antara mdia pendingin / quenching dan temperatur pemanasan terhadap nilai kekerasan grinding ball hasil pengecoran. (4) interaksi variasi media pendingin / quenching dan temperatur pemanasan yang menghasilkan nilai kekerasan yang paling optimal pada grinding ball hasil pengecoran. . Skripsi, Surakarta: Fakultas Keguruan dan Ilmu Pendidikan. Universitas Sebelas Maret Surakarta, Januari 2011. Penelitian ini dilakukan di Laboratorium Material D3 Teknik Mesin UGM sebagai tempat pengujian tingkat kekerasan. Penelitian ini menggunakan metode eksperimen. Populasi yang dipakai adalah grinding ball hasil pengecoran. Sampel diambil dengan teknik “Purposive Sampling”, dengan sembilan spesimen uji dan pengujian kekerasan dilakukan di lima titik untuk setiap spesimen. Teknik analisis data pada penelitian ini adalah ANAVA dua jalan. Hasil penelitian ini adalah: (1) Hasil uji Anava dua jalan adalah ada pengaruh perbedaan temperatur pemanasan terhadap nilai kekerasan dilihat pada hasil uji analisis data yang menyatakan bahwa Fobs = 11,98123 lebih besar daripada Ftabel = 5,25 (Fobs > Ft). (2) Tidak ada pengaruh perbedaan media quenching terhadap nilai kekerasan dapat dilihat pada hasil uji analisis data yang menyatakan bahwa Fobs = 0,60868 lebih kecil daripada Ftabel = 5,25 (Fobs < Ft). (3) Tidak ada pengaruh perbedaan interaksi antara temperatur pemanasan dan media quenching terhadap nilai kekerasan dapat dilihat pada hasil uji analisis data yang menyatakan bahwa Fobs = 1,14433 lebih kecil daripada Ftabel = 3,89 (Fobs < Ft). (4) Kombinasi variasi temperatur pemanasan 8000C dan media quenching SAE 40 W yang memghasilkan rerata kekerasan paling kecil 360,94 VHN. Dan kombinasi variasi temperatur pemanasan 8500C dan media quenching SAE 40 W yang memghasilkan rerata kekerasan paling besar 777,24 VHN. Danang Saputro. THE EFFECT OF COOLER MEDIA AND WARMING TEMPERATURE TOWARD THE HARDENESS OF GRINDING BALL AS THE RESULT OF CASTING The purpose of this study is to determine: (1) There is a difference whether the media influence cooling / quenching the value of the casting grinding ball hardness. (2) There is a difference whether the influence of heating temperature on hardness value hasi casting grinding ball. (3) There is a difference whether the interaction effect between mdia cooling / quenching and heating temperature on the value of the casting grinding ball hardness. (4) interaction variation of the cooling media / quenching and warming temperatures that produce the most optimal value of violence in the casting grinding ball. This research was conducted at the Laboratory of Engineering Materials D3 UGM as a place to test the level of violence. This research uses experimental methods. The population used is the result of casting grinding ball. Samples were taken with the technique of "purposive sampling", with nine test specimens and the hardness test performed at five points for each specimen. The data analysis technique in this research is two-way ANAVA. . Thesis, Surakarta: Faculty of Teacher Training and Education. Eleven March Surakarta University, January 2011. The results of this study were: (1) two-way Anova test result is no effect of heating temperature on the overall level of violence seen in the data analysis of test results stating that the FOBS = 11.98123 is greater than Ftable = 5.25 (FOBS> Ft.) (2) There was no effect of different quenching media on the value of hardness can be seen on the results of test data analysis which states that the FOBS = 0.60868 is smaller than Ftable = 5.25 (FOBS

×

Penulis Utama	:	Danang Saputro
Penulis Tambahan	:	-
NIM / NIP	:	X250601
Tahun	:	2011
Judul	:	Pengaruh Media Pendingin Dan Temperatur Pemanasan Terhadap Nilai Kekerasan Grinding Ball Hasil Pengecoran
Edisi	:
Imprint	:	Surakarta - F.KIP - 2011
Program Studi	:	S-1 Pendidikan Teknik Mesin Non Reguler
Kolasi	:
Sumber	:	UNS- F.KIP Prog. Pend Teknik Mesin-X.25 06 01-2011
Kata Kunci	:
Jenis Dokumen	:	Skripsi
ISSN	:
ISBN	:
Link DOI / Jurnal	:	-
Status	:	Public
Pembimbing	:	1. Suharno, S.T, M.T 2. Budi Harjanto,S.T,M.Eng
Penguji	:
Catatan Umum	:
Fakultas	:	Fak. KIP

×

File	:	Harus menjadi member dan login terlebih dahulu untuk bisa download.