Pengaruh kadar fly ash sebagai pengganti sebagian semen terhadap modulus elastisitas pada high volume fly ash – self compacting concrete (Effect of Fly Ash Content as Cement Subtitution On Elastic Modulus of High Volume Fly Ash- Self Compacting Concre
Penulis Utama
:
Dedi Septian
NIM / NIP
:
I1107041
×Pengecoran beton dengan tulangan padat atau tempat yang tidak memungkinkan menggunakan vibrator tidak menjamin tercapainya kepa¬datan secara optimal dan hanya mengandalkan sifat self-compactibility beton segar. Sifat self-compactibility menjadi dasar penggunaan Self Compacting Concrete (SCC). Penggunaan fly ash sebagai pengganti sebagian semen dalam campuran Self Compacting Concrete dengan kadar lebih dari 50% atau disebut High Volume Fly Ash Self Compacting Concrete (HVFA SCC) akan menambah kemampuan aliran beton segar , mengurangi kapur padam aktif sebagai hasil sampingan dari proses hidrasi antara semen dan air yang cenderung melemahkan beton serta menambah kepadatan beton karena butiran fly ash akan berperan sebagai filler antar agregat. Salah satu tolok ukur kepadatan suatu beton dapat silihat dari nilai modulus elastisitasnya.
Penelitian ini menggunakan metode eksperimen dengan total benda uji 27 buah berbentuk silinder dengan diameter 15 cm dan tinggi 30 cm. Variasi kadar fly ash yang ditinjau dalam penelitian ini adalah 35%, 55%, dan 65%. Kadar fly ash 35% dalam penelitian ini digunakan sebagai pembanding sesuai syarat maksimum penggunaan fly ash dalam ASTM C618-86. Pengujian modulus elastisitas mengacu rumusan dalam ASTM C 469-94 pada umur 7 hari, 28 hari dan 56 hari.
Dari hasil pengujian modulus elastisitas HVFA SCC terdapat pengaruh penggunaan fly ash semakin banyak pada campuran beton menyebabkan nilai modulus elastisitasnya cenderung rendah pada saat awal umur beton. Pada umur 7 hari, kadar fly ash 65 % memiliki nilai modulus elastisitas terendah dibanding dengan kadar fly ash yang lebih rendah, tetapi semakin lama umur beton dengan semakin banyak fly ash yang digunakan nilai modulus elastisitasnya cenderung lebih besar. Pada beton umur 56 hari dengan kadar fly ash 65% nilai modulus elastisitasnya lebih besar dibanding beton dengan kadar fly ash yang lebih rendah. Dalam rumusan ACI 318M-95 didapat rumusan hubungan kuat tekan dan modulus elastisitas HVFA SCC adalah E = 4075 untuk kadar 35 %, E = 4479 kadar 55% , dan E = 4863 kadar 65%.
Foundry fresh concrete with heavy reinforcement or places that are not allowed to use a vibrator does not guarantee the achievement of optimum density and rely solely on self-compactibility of fresh concrete properties. The property of self-compatibility becomes the basis for the use of self compacting concrete. Use of fly ash as a partial substitute for cement in the mix of self-compacting concrete with high levels of more than 50% or so-called High Volume Fly Ash Self Compacting Concrete (SCC HVFA) will increase the ability of fresh concrete flow, reduce outages calcium active as a byproduct of cement hydration process and water which tends to weaken the concrete and increase the density of fly ash concrete for grain will act as a filler between the aggregate. One measure the density of the concrete can be seen from the value of the modulus of elasticity.
This study uses an experimental method with a total of 27 test specimens with a cylindrical diameter of 15 cm and 30 cm high. Variations in content of fly ash are reviewed in this study was 35%, 55%, and 65%. Contents of 35% fly ash used in this study as a comparison according to the terms maximum use of fly ash in ASTM C618-86. Modulus of elasticity refers to the formulation of the test in ASTM C469-94 at the age of 7 days, 28 days, and 56 days.
From the test results contained HVFA SCC modulus of elasticity influence more use of fly ash in concrete mixtures cause the value of modulus of elasticity tends to be low during the early age of concrete. At the age of 7 days 65% fly ash content has a value of modulus of elasticity compared with the lowest levels of fly ash is lower, but the longer age of concrete with a growing number of fly ash used elastic modulus values tend to be larger. At the age of 56 days of concrete with fly ash content of 65% of the value of modulus of elasticity greater than concrete with fly ash content is lower. In the formulation of ACI 318M-95 formulation of the relationship obtained compressive strength and modulus of elasticity HVFA SCC is E = 4075√f’c to 35% contens, E = 4479√f’c to 55% contens, and E = 4863√f’c to 65% contens.
×
Penulis Utama
:
Dedi Septian
Penulis Tambahan
:
-
NIM / NIP
:
I1107041
Tahun
:
2012
Judul
:
Pengaruh kadar fly ash sebagai pengganti sebagian semen terhadap modulus elastisitas pada high volume fly ash – self compacting concrete (Effect of Fly Ash Content as Cement Subtitution On Elastic Modulus of High Volume Fly Ash- Self Compacting Concre