The design of hot mixture thin surfacing containing asbuton modified bitumen fro hot and erid region

Penulis Utama : Omar Mohamed Kabbash
NIM / NIP : S9413020
× Hot arid region is a region when it is characterized by a severe lack of available water and has a high temperature like Australia and Africa. In this condition, hot mix asphalt (HMA) thin surfacing is chosen for road preservation. This study is aimed to study about modified asbuton for hot mix asphalt by thin surfacing overlay. For bitumen modified, researcher used three types of asphalt (asphalt penetration 60/70, retona blend 55 and polymer SBS) specimen which be add with 5%, 5.5%, 6%, 6.5% and 7% for each sample with thickness of 30mm. Moreover, for the temperature test, it was tested at 20oC until 60oC. The specimen was tested by five test ofmarshall, indirect tensile strength (ITS), unconfined compressive strength (UCS), permeability and indirect tensile stiffness modulus (ITSM) test. The test showed that polymer SBS can be used as a binder for alternative industrial asphalt in flexible pavement at hot and arid region. Polymer SBS is good material that has same sensitivity in the different temperature. From the UCS test, polymer SBS has highest result than asphlat penetration 60/70 and retona blend 55. Result of marshall test showed that Polymer SBS more stable than asphalt penetration 60/70 and retona blend 55. Polymer SBS also has the highest density. Whereas for ITS test, permeability test and ITSM test, retona blend 55 showed the highest result. Retona blend 55 has the better result for the test average that was conducted in this study.
×
Penulis Utama : Omar Mohamed Kabbash
Penulis Tambahan : -
NIM / NIP : S9413020
Tahun : 2014
Judul : The design of hot mixture thin surfacing containing asbuton modified bitumen fro hot and erid region
Edisi :
Imprint : Surakarta - Pascasarjana - 2014
Program Studi : S-2 Teknik Sipil
Kolasi :
Sumber : UNS-Pascasarjana Prodi. Teknik Sipil-S. 9413020-2014
Kata Kunci :
Jenis Dokumen : Tesis
ISSN :
ISBN :
Link DOI / Jurnal : -
Status : Public
Pembimbing : 1. Ir. Ary Setyawan
2. Dr. Dewi Handayani, ST .MT
Penguji :
Catatan Umum :
Fakultas : Sekolah Pascasarjana
×
File : Harus menjadi member dan login terlebih dahulu untuk bisa download.