ABSTRAK
Penelitian ini bertujuan untuk mengetahui pengaruh ketebalan dan penambahan
partikel nano pada perekat terhadap kekuatan tarik geser sambungan tumpang
tunggal antara alumunium dan komposit. Variasi ketebalan perekat yang
digunakan adalah 0,1; 0,2; 0,3; 0,4; 0,5; 0,6; 0,7; 0,8; 0,9 dan 1 mm. Sambungan
dibuat menggunakan proses penekanan dengan tekanan 0,1 MPa setiap satu
spesimen. Pembuatan spesimen uji tarik geser mengacu pada ASTM D 1002.
Hasil pengujian menunjukkan variasi ketebalan perekat mempengaruhi kekuatan
tarik geser sambungan. Sambungan dengan ketebalan 0,5 mm memiliki kekuatan
tarik geser tertinggi pada perekat epoksi dan epoksi/nano silika yaitu masingmasing
sebesar 3,58 MPa dan 5,43 MPa. Penambahan partikel nano silika pada
perekat meningkatkan kekuatan tarik geser rata-rata sebesar 30,87 %. Keberadaan
partikel nanosilika pada perekat dapat memperkuat perekat. Partikel nano silika
juga dapat memasuki celah adherend akibat perlakuan kertas abrasif sehingga
memperkuat ikatan antara perekat dengan permukaan adherend.
Kata kunci: Nano Silika, Epoksi, Kekuatan Tarik Geser, Sambungan Tumpang
Tunggal
ABSTRACT
The objective of this research is to investigate the effect of thickness and the
addition of nano particles in the adhesive on the shear strength of a single lap
joint between aluminum and composite. The thickness variations of adhesive used
were 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9 and 1 mm. The joint was made using a
process with a pressure of 0,1 MPa each specimen. The formation of specimen for
shear testing employed ASTM D 1002. The result of the research shows that the
adhesive thickness variations affect the shear strength of the joint. The joint with a
thickness of 0.5 mm has a highest shear strength of epoxy and epoxy/nano silica
adhesive respectively by 3.58 MPa and 5.43 MPa. The addition of nano particles
of silica in the adhesive increases the shear strength average of 30.87%. The
existence of particles in the adhesive can reinforce nanosilika adhesive. Nano
silica particles can also enter the gap adherend due to treatment of abrasive
paper that reinforce the bond between the adhesive to the surface of the adherend.
Keywords: Nano Silica, Epoxy, Shear Strength, Single Lap Joint

File Dokumen Tugas Akhir : abstrak.pdf
Harus menjadi member dan login terlebih dahulu untuk bisa download.
IMG_20150604_0001.pdf
Halaman Judul.pdf
Bab 1.pdf
Bab 2.pdf
Bab 3.pdf
Bab 4.pdf
Bab 5.pdf
File Dokumen Karya Dosen : -
Status : Public
Pembimbing : 1. Prof. Dr. Kuncoro Diharjo, S.T., M.T.
2. Dr. Triyono, S.T., M.T.
Catatan Umum :
Fakultas : Pascasarjana