Penulis Utama : Ratna Dwi Sejati
Penulis Tambahan : -
NIM / NIP : M0211063
Tahun : 2015
Judul : Fabrikasi dan Karakterisasi Preform Fiber Optik TZBN : Nd
Edisi :
Imprint : Surakarta - FMIPA - 2015
Kolasi :
Sumber : UNS-FMIPA Jur. Pendidikan Fisika-M0211063-2015
Subyek : TZBN : ND
Jenis Dokumen : Skripsi
ISSN :
ISBN :
Abstrak :

ABSTRAK
Penelitian ini bertujuan untuk melakukan fabrikasi preform kaca tellurite
berbentuk kotak dan core serta melakukan karakterisasi pada kaca yang dihasilkan
berupa densitas kaca, indeks bias, absorbsi dan transmitansi dan kebocoran berkas
cahaya pada preform sampel kaca. Kaca tellurite yang digunakan adalah TZBN
(Tellurium Zinc Bismuth Natrium Oksida) dengan komposisi (%mol) 60TeO2
(34-x) ZnO 2 Bi2O3 4Na2O xNd2O3 (dengan variasi % mol x=0 ; 0.5 ; 1 ;
1.5). Fabrikasi telah berhasil dilakukan dengan menggunakan metode melt
quenching. Rapat massa kaca telah diukur menggunakan metode Archimedes
diperoleh hasil (5.45 5.58) gram/cm3. Indeks bias kaca diukur menggunakan
metode sudut Brewster pada panjang gelombang 746.191 nm menghasilkan
indeks bias (1.81-19.2). Absorbsi diukur menggunakan UV-Vis spektrometer
Perkin Elmer Lambda 25 dengan panjang gelombang (200-800) nm. Kebocoran
berkas cahaya pada preform diukur menggunakan laser merah dengan panjang
gelombang 746.191 nm. Hasil karakterisasi menunjukkan bahwa rapat massa dan
indeks bias kaca mengalami kenaikan seiring dengan kenaikan konsentrasi dadah
ion Nd pada kaca TZBN:Nd. Melalui pengukuran spektrum UV-Vis menunjukkan
bahwa terjadi penyerapan dengan intensitas yang tinggi pada panjang gelombang
431 nm, 473 nm, 515 nm, 527 nm, 586 nm, 628 nm, 684 nm, dan 749 nm dan
penyerapan tertinggi berada pada panjang gelombang 586 nm.
Kata kunci : Preform, TZBN:Nd, rapat massa, indeks bias, Spektroskopi UV-Vis.
ABSTRACT
This research aims to do the fabrication of tellurite glass box-shaped
preform and core as well as perform characterization of glass produced in the
form of glass density, refractive index, the absorption and transmitansi and the
leakage of beam of light on the sample glass preform. Tellurite glass was TZBN
(Sodium Bismuth Tellurium Oxide Zinc) with composition (% mol) 60TeO2
(34-x) ZnO 2 Bi2O3 4Na2O xNd2O3 (with variation% mol x = 0.5; 0; 1; 1.5).
Fabrication has been successfully performed using melt quenching method. Glass
density had measured using Archimedes method obtained result (5.45 5.58)
gram/cm3 . Refractive index of glass had measured using Brewster angle method
at 746.191 nm wavelength generated a refractive index (1.81-19.2). Absorption
was measured using an Uv-Vis spectrophotometer Perkin Elmer Lambda 25 with
a wavelength of (200-800) nm. Loss of light beam on preform was measured
using a red laser with a wavelength of 746.191 nm. Characterization of the results
showed that density and the refractive index of glass increased along with the
increase concentration of ionic doped Nd on glass TZBN: Nd. UV-Vis spectra
measurement indicate that absorption occurs at wavelength of 436 nm, 470 nm,
532 nm, 530 nm, 595 nm, 590 nm, 700 nm, and 750 nm and the highest
absorption at 589 nm wavelength.
Keywords: Preform, TZBN: Nd, density, refractive index, UV-Vis
Spectroscopy.

File Dokumen : abstrak.pdf
Harus menjadi member dan login terlebih dahulu untuk bisa download.
IMG_20151207_0006.pdf
Bab 0.pdf
Bab 1.pdf
Bab 2.pdf
Bab 3.pdf
Bab 4.pdf
Bab 5.pdf
File Dokumen : -
Status : Public
Pembimbing : 1. Dra. Riyatun, M.Si,
2. Lita Rahmasari, S.Si, M.Si,
Catatan Umum :
Fakultas : Fak. MIPA