Penulis Utama : Lidya Nur De Vega
Penulis Tambahan : -
NIM / NIP : M0211047
Tahun : 2015
Judul : Analisis Morfologi Permukaan dan Penentuan Mobilitas Pembawa Muatan Lapisan Klorofil Spirulina SP Hasil Deposisi Spin Coating
Edisi :
Imprint : Surakarta - FMIPA - 2015
Kolasi :
Sumber : UNS-FMIPA Jur. Fisika-M0211047-2015
Subyek : LAPISAN KLOROFIL
Jenis Dokumen : Skripsi
ISSN :
ISBN :
Abstrak :

ABSTRAK
Karakteristik morfologi permukaan lapisan klorofil hasil AFM (Atomic Force Microscopy) telah dianalisis. Analisis morfologi dilakukan menggunakan program WSxM 5.0 Develop 7.0 meliputi analisis 2D (2 dimensi), analisis 3D (3 dimensi), histogram ukuran partikel dan profile permukaan dari lapisan tipis. Lapisan klorofil ditumbuhkan dengan metode spin coating pada substrat glass coated ITO. Pada proses penumbuhan dilakukan variasi jumlah perulangan lapisan (N). Hasil pengamatan morfologi dengan AFM (Atomic Force Microscopy) menjelaskan bahwa lapisan tipis dengan N = 5 memiliki permukaan yang lebih rata dibandingkan dengan N = 3 akibat adanya proses inter molekular interaksi. Ukuran molekul penyusun lapisan klorofil membentuk distribusi Gaussian. Pada hasil pengamatan dari kurva profil permukaan diperoleh ketebalan lapisan berturut-turut sebesar 281,7 dan 372,6 nm untuk N = 3 dan N = 5. Karakteristik selanjutnya adalah karakteristik kurva I – V dari lapisan tipis. Kurva ini merupakan kurva hubungan arus dan tegangan dari lapisan tipis pada suhu ruang. Hasil dari kurva I – V ini adalah berupa perolehan gradien yang kemudian digunakan untuk mengukur mobilitas pembawa muatan lapisan tipis. Variasi jumlah pelapisan dan jumlah kecepatan putar yang dilakukan telah memberikan pengaruh terhadap mobilitas yang dihasilkan. Peningkatan jumlah lapisan menunjukkan adanya peningkatan mobilitas (μ) pembawa muatan dan peningkatan jumlah kecepatan putar menunjukkan penurunan mobilitas dari pembawa muatan.
Kata Kunci: Lapisan Klorofil, Spin Coating, Morfologi Permukaan, AFM, Mobilitas.
ABSTRACT
Surface morphological characteristic of chlorophyll layer have been analized.  Morphological surface have been done by WSxM 5.0 Develop 7.0 program including 2D (2 dimension), 3D (3 dimension), histogram of size distribution and surface profile analysis. Chlorophyll layer deposited by spin coating methods on a glass coated ITO substrates. Layer variation (N) performed in this deposition. Results of morphological observation by AFM (Atomic Force Microscopy) explains that a thin layer with N = 5 has a flatter surface than with N = 3 due to inter molecular interaction process. The molecular size of the chlorophyll layers form a Gaussian distribution. From the profile curves, thickness of the layer were obtained as 281.7 nm and 372.6 nm for N =3 and 5 respectively. Characteristics of I – V curve has been done for chlorophyll layer. I – V curve explained the relationship between current and voltage. Gradient of this I – V curve than used for mobility measurement of chlorophyll layer. Layer and spin rate variation performed influenced mobility. Increasing of layer number raise the  mobility (μ) and increasing of spin rate showed the decrease of mobility.
Keywords: Chlorophyll layer, Spin coating, Surface morphology, AFM, mobility.

File Dokumen Tugas Akhir : abstrak.pdf
Harus menjadi member dan login terlebih dahulu untuk bisa download.
IMG_20151216_0001.pdf
1.cover daftar isi abstrak_revised.pdf
Bab 1.pdf
Bab 2.pdf
Bab 3.pdf
Bab 4.pdf
Bab 5.pdf
File Dokumen Karya Dosen : -
Status : Public
Pembimbing : 1. Dr.Eng. Budi Purnama., S.Si., M.Si
2. Utari., S.Si., M.Si
Catatan Umum :
Fakultas : Fak. MIPA