Penulis Utama : Muhammad Yassin T.i.p
Penulis Tambahan : -
NIM / NIP : I1412013
Tahun : 2015
Judul : Pengaruh Jenis Adhesive terhadap Kekuatan Mekanik Komposit Sandwich CANTULA-rHDPE
Edisi :
Imprint : Surakarta - F. Teknik - 2015
Kolasi :
Sumber : UNS-F. Teknik Jur. Teknik Mesin-I1412013-2015
Subyek : KEKUATAN MEKANIK
Jenis Dokumen : Skripsi
ISSN :
ISBN :
Abstrak :

ABSTRAK
Sifat komposit sandwich dipengaruhi oleh sifat core, sifat skin dan ikatan yang terbentuk antara core dan skin. Kualitas ikatan tergantung pada jenis adhesive yang digunakan untuk mengikat antara skin dan core. Sehingga, studi tentang adhesive yang mampu menghasilkan kekuatan mekanik terbaik perlu dilakukan. Penelitian ini difokuskan untuk mengetahui pengaruh jenis adhesive terhadap kekuatan bending dan kekuatan geser komposit sandwich cantula-rHDPE. Adhesive yang digunakan dalam penelitian ini adalah epoxy, chloroprene dan cyanoacrylate. Skin terbuat dari serbuk recycled High Density Polyethylene (rHDPE), sedangkan core terbuat dari serat cantula dan rHDPE. Proses pembuatan skin dan core dilakukan menggunakan hot press. Parameter proses yang digunakan meliputi temperatur proses 170oC, waktu penahanan 15 menit, tekanan pengepresan skin 50 bar dan core 40 bar. Prosedur pengujian bending dan geser mengacu pada ASTM C 393 dan ASTM C 273. Patahan spesimen dianalisa dengan menggunakan foto makro. Hasil pengujian menunjukkan bahwa jenis adhesive berpengaruh pada kekuatan bending dan kekuatan geser komposit sandwich cantula-rHDPE.  Kekuatan bending tertinggi 21,85 MPa  diperoleh dengan adhesive cyanoacrylate dan nilai terendah 8,48 MPa pada adhesive chloroprene. Sedangkan kekuatan  geser  tertinggi sebesar 5,47 MPa pada adhesive cyanoacrylate dan nilai terendah 2,84 MPa pada adhesive chloroprene.
Kata kunci: Komposit sandwich cantula-rHDPE, adhesive, kekuatan bending, kekuatan geser.
ABSTRACT
The characteristic of sandwich composite is influenced by the characteristic of core, skin and bond which are formed between core and skin. The quality of bond depends on the adhesive type that is used to bind skin and core. Because of that, the study of adhesive that is capable producing the best mechanical strength needs to be done. This research is focused to know the effect of adhesive type on the flexural strength and shear strength  of cantula r-HDPE sandwich composite. The adhesive which is used in this research are epoxy, chloroprene and cyanoacrylate. The skin is made from the powder of recycled High Density Polyethylene (rHDPE), while the core is made from the fiber of cantula and r-HDPE. The making process of skin and core is doing by hot press. The process parameter used are the process temperature 170¬¬oC, holding time 15 minutes, the pressing tension skin 50 bars and core 40 bar. The procedure of flexural and shear testing are refers to ASTM C 393 and ASTM C 273. The facture of the specimen can be analysed stereo zoom microscope. The test result shows that the adhesive type influences on flexural strength and shear strength cantula r-HDPE sandwich composite. The highest flexural strength is 21.85 MPa on cyanoacrylate adhesive and the lowest of it is 8.48 MPa on chloroprene adhesive. While the highest shear strength is 5.47 MPa on cyanoacrylate adhesive and the lowest of it is 2.84 MPa on chloroprene adhesive.
Key words: cantula r-HDPE sandwich composite, adhesive, flexural strength, shear strength.

File Dokumen Tugas Akhir : abstrak.pdf
Harus menjadi member dan login terlebih dahulu untuk bisa download.
Scan_2.pdf
depan_1.pdf
bab1_1.pdf
bab2_1.pdf
bab3_1.pdf
bab4_1.pdf
bab5_1.pdf
File Dokumen Karya Dosen : -
Status : Public
Pembimbing : 1. Teguh Triyono, ST., M. Eng
2. Ir.Wijang Wisnu Raharjo, MT
Catatan Umum :
Fakultas : Fak. Teknik