Judul : Karakterisasi Bahan Superkonduktor Pb3Sr4Ca3Cu6Ox dengan Variasi Suhu Sintering Menggunakan Metode Reaksi Padatan
Edisi :
Imprint : Surakarta - FMIPA - 2015
Kolasi :
Sumber : UNS-FMIPA Jur. Fisika-M0211023-2015
Subyek : REAKSI PADATAN
Jenis Dokumen : Skripsi
ISSN :
ISBN :
Abstrak :

ABSTRAK
Karakterisasi bahan superkonduktor Pb3Sr4Ca3Cu6Ox dengan variasi suhu sintering menggunakan metode reaksi padatan telah dilakukan. Metode yang digunakan dalam karakterisasi bahan superkonduktor PSCCO adalah metode reaksi padatan dengan variasi suhu sintering, yaitu: 850 oC, 860 oC, 870 oC dan 880 oC. Karakterisasi yang dilakukan meliputi uji Meissner dan pengukuran suhu kritis. Uji Meissner dilakukan menggunakan nitrogen cair sebagai pendingin sampel. Pada pengukuran suhu kritis digunakan metode Four Point Probe dengan menggunakan peralatan Cryogenic Magnet “Cryotron FR” buatan Oxford. Pengujian suhu kritis dilakukan menggunakan cairan helium dengan suhu yang dapat dicapai sekitar 4,2 K. Dari pengujian yang telah dilakukan, diperoleh bahwa suhu sintering mempengaruhi efek Meissner serta nilai suhu kritis bahan superkonduktor. Dari pengujian yang telah dilakukan, didapatkan hasil bahwa sampel yang dikarakterisasi dengan suhu sintering 860 oC memiliki nilai suhu kritis paling tinggi dan terjadi efek Meissner lemah. Nilai suhu kritis yang didapatkan pada sampel superkonduktor dengan suhu sintering 860 oC adalah sekitar 49,9 K (-223,1 oC).
Kata kunci : superkonduktor PbSrCaCuO, efek Meissner, suhu kritis, metode reaksi padatan
ABSTRACT
Characterization material superconductors Pb3Sr4Ca3Cu6Ox with temperature variations sintering uses solid state reaction method have managed to be done. Method used in characterization of PSCCO superconductors is the solid state reaction with temperature variations sintering, namely 850 oC, 860 oC, 870 oC and 880 oC. Characterization was about the Meissner test and critical temperature measurement. Meissner test conducted using liquid nitrogen as a coolant sample. On critical temperature measurement used method Four Point Probe using Cryogenic Magnet equipment "Cryotron FR" artificial Oxford. Critical temperature measurement using helium liquid with a temperature that can be reached about 4.2 K. From the testing that has been done, found that the sintering temperature affects the Meissner effect and the value of the critical temperature of the material superconductors. From the testing that has been done, showed that sample is syntesized with sintering temperature of 860 oC has the highest critical temperature value and occurs weak Meissner effect. Critical temperature values obtained on samples with sintering temperature superconductors 860 oC was about 49.9 K (-223.1 oC).
Keywords : superconductor PbSrCaCuO, Meissner effect, critical temperature, solid state reaction method

File Dokumen : abstrak.pdf
Harus menjadi member dan login terlebih dahulu untuk bisa download.
IMG_20160219_0001.pdf
Bab 0.pdf
Bab 1.pdf
Bab 2.pdf
Bab 3.pdf
Bab 4.pdf
Bab 5.pdf
File Dokumen : -
Status : Public
Pembimbing : 1. Drs. Usman Santosa, MS
2. Dwi Teguh Rahardjo, S.Si., M.Si.
Catatan Umum :
Fakultas : Fak. MIPA