Judul : Pemanfaatan Lumpur Geothermal (Geothermal Sludge) untuk Pengganti Sebagian Semen terhadap Kuat Tekan Mortar sebagai Suplemen Bahan Ajar Mata Kuliah Teknologi Beton Program Studi Pendidikan Teknik Bangunan UNS
Edisi :
Imprint : Surakarta - FKIP - 2015
Kolasi :
Sumber : UNS-FKIP Jur. Pendidikan Teknik Bangunan-K1511019-2015
Subyek : LUMPUR
Jenis Dokumen : Skripsi
ISSN :
ISBN :
Abstrak :

ABSTRAK
Penelitian yang mensubstitusi semen dengan lumpur geothermal dalam konteks volume bertujuan untuk mengetahui komposisi adukan yang paling ideal bila ditinjau dari segi kuat tekan pada sampel mortar. Dalam penelitian ini, dibuat 4 variasi mix desain yaitu adukan 1 (100% PC; 0% LG), 2 (90% PC; 10% LG), 3 (80% PC; 20% LG) dan 4 (70% PC; 30% LG. Perbandingan berat antara PC dengan pasir adalah 1 : 2,75 dengan faktor air semen mendekati 0,485. Semen yang digunakan dalam penelitian ini adalah semen portland tipe I dengan benda uji dites dalam umur 28 dan 56 hari.
Bila ditinjau dari segi kuat tekan, penggunaan lumpur Geothermal berpengaruh terhadap kuat tekan sampel mortar yang dibuktikan dengan perhitungan nilai korelasi. Kuat tekan optimal sampel diketahui dari data uji dengan variasi lumpur geothermal sebesar 20%. Pada adukan ini, kuat tekan yang dihasilkan sebesar 27,093 MPa pada umur mortar 28 hari dan 27,266 MPa pada umur mortar 56 hari.
Kontribusi peneliti untuk bidang pendidikan yaitu Bahan ajar yang dihasilkan setelah penelitian ini berupa suplemen bahan ajar tentang pemanfaatan lumpur geothermal untuk pengganti sebagian semen ditinjau dari kuat tekan mortar atau lebih jelasnya modul untuk mata kuliah Teknologi Beton semester III Program Studi Pendidikan Teknik Bangunan UNS pada kompetensi dasar 4 materi mortar.
Kata Kunci : Lumpur Geothermal, Pengganti Semen, Kuat Tekan Mortar, Bahan Ajar Mortar
ABSTRACT
The study was substituting cement with geothermal sludge in context volume to find the most ideal if mortar composition in terms of the compressive strength of the mortar samples. In this research, made 4 variations of mix designs that stirring 1 (100% PC; 0% GS), 2 (90% PC, 10% GS), 3 (80% PC, 20% GS) and 4 (70% PC; 30 % GS). The ratio weight between the PC and the sand is 1: 2.75 with cement water factor approaching 0.485. The cement that used in this study were Portland cement type I with test specimens were tested at the age of 28 and 56 days.
When viewed in terms of compressive strength, the use of geothermal sludge take effect towards compressive strength mortar samples as evidenced by the correlation value of calculation. Optimal compressive strength known sample of test data with geothermal sludge variation of 20%. In this stirring, compressive strength generated at 27.093 MPa at the age of 28 days mortar and 27.266 MPa at the age of 56 days mortar.
Contributing researchers to the field of education, namely teaching materials produced after this research is a supplement teaching materials on the use of sludge geothermal for partial replacement of cement in terms of the compressive strength of mortar or more details modules for the course Concrete Technology III Semester Study Program Building Techniques UNS on basic 4th competencies in mortar material.
Keyword : Geothermal Sludge, Cement Subtitution, Mortar Compressive Strength, Mortar Teaching Materials

File Dokumen : abstrak.pdf
Harus menjadi member dan login terlebih dahulu untuk bisa download.
IMG_20160222_0001.pdf
Cover DLL.pdf
BAB I INDAH.pdf
BAB II INDAH.pdf
BAB III INDAH.pdf
BAB IV indah.pdf
BAB V indah.pdf
File Dokumen : -
Status : Public
Pembimbing : 1. Rima Sri Agustin, S.T.,M.T.
2. Eko Supri Murtiono, S.T.,M..T.
Catatan Umum :
Fakultas : Fak. KIP