Judul : Pengaruh Variasi Laju Pendinginan terhadap Kekuatan Mekanik Material Komposit Serat Kenaf-Polypropylene
Edisi :
Imprint : Surakarta - F. Teknik - 2015
Kolasi :
Sumber : UNS-F. Teknik Jur. Teknik Mesin-I1410036-2015
Subyek : LAJU PENDINGIN
Jenis Dokumen : Skripsi
ISSN :
ISBN :
Abstrak :

ABSTRAK
Komposit serat alam merupakan bahan alternatif untuk menggantikan
komposit serat sintetis. Kekuatan mekanik komposit serat alam dengan matrik
polimer termoplastik sangat dipengaruhi oleh kondisi proses pembuatan. Tujuan
dari penelitian ini adalah untuk mengetahui pengaruh laju pendinginan terhadap
kekuatan mekanik material komposit serat kenaf-polypropylene.
Material komposit serat kenaf-polypropylene diproses dengan metode hot
press forming. Temperatur yang digunakan adalah 165 oC pada tekanan 50 bar.
Variasi laju pendinginan yang dilakukan adalah 0,54 oC/menit; 1,68 oC/menit, dan
53,19 oC/menit. Kekuatan mekanik yang diuji adalah kekuatan tarik, kekuatan
bending dan kekuatan impak. Strukutur mikro setiap variasi spesimen uji diamati
menggunakan mikroskop polarisasi. Permukaan patahan spesimen uji diamati
dengan foto SEM.
Hasil pengujian menunjukkan kekuatan tarik dan bending menurun pada
laju pendinginan lebih cepat Kekuatan tarik dan kekuatan bending tertinggi
diperoleh pada komposit dengan laju pendinginan 0,54 oC/menit. Kekuatan impak
tertinggi diperoleh pada komposit dengan laju pendinginan 53,19 oC/menit.
Kata Kunci: Laju Pendinginan, Serat kenaf, Polypropylene, Foto Mikro, SEM,
Sifat Mekanik.
ABSTRACT
Natural fibre composites are alternative material to replace the synthetic
fibre composites. The mechanical strength of natural fiber composites is
influenced by the condition of the manufacturing process. The aim of this study is
to determine the effect of cooling rate on mechanical strength of kenaf fibrepolypropylene
composite.
Kenaf fibre-polypropylene composites were processed by hot press
forming method. The temperature hot press was 165 oC at a 50 bar of pressure.
The variation of cooling rate were 0,54 oC/min; 1,68 oC/min and 53,19 oC/min.
Mechanical strength of composites were determined by tensile, bending and
impact test. Micro structure of the specimens was observed using polarization
microscope. The fracture surface of specimens was observed by SEM photograph.
The testing results show that tensile and bending strength are decrease on
the faster cooling rate. The highest tensile and bending strength of kenaf fibrepolypropylene
composites are obtained at the cooling rate 0,54 oC/min. The
highest impact strength is obtained at cooling rate 53,19 oC/min.
Keyword: Cooling rate, kenaf fibre, Polypropylene, Mechanical
characteristic, Micro photograph, SEM.

File Dokumen : abstrak.pdf
Harus menjadi member dan login terlebih dahulu untuk bisa download.
IMG_20160222_0001.pdf
cover.pdf
Bab I Pendahuluan.pdf
Bab II Dasar Teori.pdf
Bab III Metode Penelitian.pdf
BAB IV Hasil dan Analisa.pdf
Bab V Penutup.pdf
File Dokumen : -
Status : Public
Pembimbing : 1. Heru Sukanto ST., MT.
2. Ir. Wijang Wisnu Raharjo, MT.
Catatan Umum :
Fakultas : Fak. Teknik